CJT_211-2005 聚合物基复合材料检查井盖

已J 中华人民共和国城镇建设行业标准 CJ/T 211-2005 聚合物基复合材料检查井盖 Inspection manhole lid made of polymer matrix composites 2005-05-16发布 2005-10-01实施 中华人民共和国建设部 发 布 曰/T 211-2005 目 次 前言 ················································································································⋯⋯ m 1 范围 ··············································································································⋯⋯ 1 2 规范性引用文件 ································································································⋯⋯ 1 3 术语 ···············································································································⋯⋯ 1 4产品规格、编号和承载等级说明·······································································⋯⋯‘’“·’3 5 技术要求 ········································································································⋯⋯ 3 6试验装置及试验方法 ·························································································⋯⋯4 7 检验规则 ·········································································································⋯⋯ 6 8标志、合格证和贮存、运输 ····················································································⋯⋯7 CJ/T 211-2005 前 言 聚合物基复合材料检查井盖经过多年实践，因其独有的一些特点，现已在全国各地得到广泛应用。 鉴于各个城市、各部门所制定的使用标准不统一，阻碍了聚合物基复合材料产品的进一步发展，为了规 范聚合物基复合材料检查井盖的使用，根据废弃物资源化国家工程研究中心多年的研究成果和生产实 践，在广泛征求市政设计、产品维护等部门以及众多施工单位、生产厂家的意见的基础上，借鉴铸铁井盖 标准，特制定本标准。 本标准由建设部标准定额研究所提出。 本标准由建设部给水排水产品标准化技术委员会归口。 本标准由废弃物资源化国家工程研究中心、中国物资流通技术开发协会、上海市市政工程研究院、 上海市市政工程行业协会、西安市市政设计研究院、广西城乡规划设计院、南宁市城市规划设计院、重庆 市设计院、成都市城市建设科学研究院起草。 本标准主要起草人:孙可伟、李如燕、赵众、牟惟仲、吴初航、顾民治、杨新义、林吉中、陆际汉、 胡金兰、汤浩、张劲文。 CJ/T 211-2005 聚合物基复合材料检查井盖 范 围 本标准规定了聚合物基复合材料检查井盖的分类、承载等级、技术要求、试验方法、检验规则及标 志等。 本标准适用于安装在城市道路、公路上的各种检查井盖，也适用于安装在其他机动车和非机动车可 能行驶或停放的地面上的各种检查井盖。同时也适用于安装在人行道、绿化用地上的各种检查井盖。 规范 性引用文件 下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有 的修改单(不包括勘误的内容)或修订版均不适用于本标准，然而，鼓励根据本标准达成 协议 离婚协议模板下载合伙人协议 下载渠道分销协议免费下载敬业协议下载授课协议下载 的各方研究 是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本标准。 GB 6414-1999 铸件 尺寸公差与机械加工余量 GB 8810 硬质泡沫塑料吸水率试验方法 GB/T 1040 塑料拉伸试验方法 GB/T 1041 塑料压缩性能试验方法 GB/T 1043 硬质塑料简支梁冲击试验方法 GB/T 9341 塑料弯曲试验方法 GB/T 16422. 2-1999 塑料实验室光源暴露试验方法 第2部分:氮弧灯 CJ/T 3012-1993 铸铁检查井盖 CJJ 37-90 城市道路设计规范 术语 3. 1 检查井 manhole 通往地下设施(如自来水、排水、电信、电力、燃气、热力、消火栓、阀门、环境卫生等)的出人口。 3.2 检查井盖 manhole lid 检查井口的封闭物，由支座和井盖组成。 3.2.1 支座 set 检查井盖中固定于检查井口的部分，用于安放井盖。 3.2.2 井盖 lid 检查井盖中未固定部分。其功能是封闭检查井口，需要时能够开启。 3.3 嵌入深度 inlaid depth 支座支承面 至支座顶 面的高度 。如图 1所示 A值 。 CJ/T 211-2005 引盖 支座 图 1 缝宽a width of aperture 支座与井盖之间的间隙，a=a, +az，见图 3.5 支座支承面 supporting face of set 支承井盖的支座平面，其宽度如图1中的b值。 3. 6 井盖接触面 interface for manhole lid 井盖与支座支承面相接触 的平面 3. 7 检查井盖净宽 D(mm) net width of manhole lid (D, mm) 支座孔口的最大内切圆直径。见图1,图2 一 二 图 2 井盖公称直径 nominal diameter of manhole lid 井盖上沿外圆的直径，如图1中的Z值 井盖锥度 taper of manhole lid 井盖上下沿外圆形成的锥度，如图3中的6角的正切值tgoo 井盖上沿 CJ/T 211-2005 3. 10 试验载荷 testing load 在测试检查井盖承载能力时规定施加的荷载 3. 11 聚合物基复合材料 Polymer matrix composites 聚合物基复合材料是利用聚合物和各种颗粒、纤维、金属等填充增强材料，通过少量添加剂及一定 工艺的作用生产出的材料。聚合物基复合材料的主要原料也可用各种废弃聚合物及废弃的颗粒、纤维 代 替 产品规格 、编号和承载等级说明 4. 1 产品规格 4.1.1 重型 :D500,D600cD700; 4. 1.2 普型;D500,D600,D700; 4. 1.3 轻型:1)500,D600,D700 4.2 产品编号 聚合物基复合材料检查井盖的编号由产品代号(JJG);结构形式:单层(D)、双层(S);主要参数:检 查井盖净宽(MM);承载等级:重型(Z)、普型(P) ;轻型(Q);四部分组成。 ]一口一口一 口 承载等级:重型(Z)、普型(P)、轻型(Q) 主要参数:检查井盖净宽(mm) 结构形式:单层(D)、双层(S) 产品代号:(JJG) 标记示例 JJG-D- 700-Z JJG一产品代号;D一单层;700一检查井盖净宽(mm) ; Z一重型。 4. 3 承载等级说明 聚合物基复合材料检查井盖按其承载能力不同主要分为重型(Z)、普型(P)、轻型(Q)三个等级(见 表 关于同志近三年现实表现材料材料类招标技术评分表图表与交易pdf视力表打印pdf用图表说话 pdf 1)0 表 1 等级 标 志 对应最高城市道路分类等级 参考设置场合 重型 z 快速路以上 货运站、码头等重型车较多的道路、场地 普型 P 决速路 车流量大的机动车行驶、停放的道路、场地 轻型 Q 次干路 工级 小型车慢速行走的道路、场地，居民小区，绿地等一般场所 5 技术要求 原材料 聚合物基复合材料检查井盖主要使用聚合物和填充增强材料制作: a) 聚合物:各种高分子材料及其再生品; b) 填充增强材料:各种颗粒状、纤维状材料及其再生品，各种金属及构件。 聚合物基复合材料检查井盖的形状宜为圆形，也可以是矩形 CJ/T 211-2005 5.3 井盖与支座间的缝宽应符合表2的要求，井盖上沿尺寸大于下沿尺寸，锥度宜为1:20-1: 表 2 检查井盖净宽 缝宽 a= a, I-az D (1-2) %D 注:锥度较大时，a值宜相对取小一些;锥度较小时，a值宜取大些. 5.4 支座支承面的宽度应)4%D(检查井盖净宽)且不应小于10 mmo 5.5 井盖的嵌人深度。重型检查井盖不应小于70 mm，普型、轻型检查井盖不应小于50 mm. 5.6 井盖的最小重量。每个井盖至少应达到下表所示的重量，见表3e 表 3 D500 D600 D700 重型井盖最小重量/kg 30 35 40 普型井盖最小重量/kg 25 30 35 轻型井盖最小重量/kg 20 25 30 5.7 井盖表面应有凸起的防滑花纹。凸起高度不应小于3 mm, 5.8 井盖与支座表面应压制平整，不应有裂纹、凹凸不平等影响井盖使用性能的缺陷。 5.9 井盖与支座装配结构尺寸应符合GB 6414的要求。其公差等级不应低于GB 6414-1999中 CT10的规定并保证井盖与支座的互换性。 5.10 检查井盖的承载能力和破坏载荷应符合表4的规定。 表 4 检查井盖等级 试验载荷(kN) 破坏载荷〔kN) 允许残留变形〔mm) 重 型 270 妻360 (1/500)D 普 型 180 妻250 (1/500)D 轻 型 90 )130 (1/500)D 试验装置及试验方法 聚合物基复合材料检查井盖应按复合材料主要性能指标、承载性能、耐热性能、抗冻性能、耐候性 能、抗疲劳性能等检测项目进行试验。 62 聚合物基复合材料主要性能指标见表So 表 5 项 目 性 能 指 标 制样测试标准 弯曲强度 平均值)22 MPa，单块最小值妻18 MPa GB/T 9341 冲击强度 平均值)10' J/m'，单块最小值)6X10' J/m' GB/T 1043 压缩强度 平均值)25 MPa,单块最小值)20 MPa GB/T 1041 拉伸强度 平均值)10 MP. ，单块最小值)8 MPa GB/T 1040 弹性模量 平均值)1 000 MPa,单块最小值)600 MPa(弯曲弹性模量) GB/ T 9341 吸水率 <1% GB 8810 耐酸性 试样在 20%硫酸溶液中浸泡 48 h,表面无明显腐蚀。质量损失<1% 耐碱性 试样在 20%氢氧化钠溶液中浸泡 48 h，表面无腐蚀。质量损失<1% 耐热 性 破坏载荷下降簇5% 见本标准 6.4 耐候 性 破坏载荷下降簇5% 见本标准 6.6 cl/T 211-2005 6.3 承载性能试验 6.3. 1 应按成套产品进行承载能力试验 6.3.2 加载设备:加载设备所能施加的载荷不应小于500 kN，其台面尺寸应大于检测井盖支座最外缘 尺寸 测力仪器的误差应低于士200，加载试验装置如图40 加载 台面 图 4 6.3.3 试验装置附件 a) 刚性垫块 刚性垫块尺寸应为，直径356 mm、厚度等于或大于40 mm、上下表面平整，见图5 b) 橡胶垫片 在刚性垫块与井盖之间放置一弹性橡胶垫片，垫片的平面尺寸应与刚性垫块相同，垫片厚度应为 6 mm-10 mm, }l IV 1X 45 图 5 6.3.4 试验程序 6.3.4. 1 调整刚性垫块的位置，使其中心与井盖的几何中心重合 6.3.4.2 在施加2/3试验荷载后，井盖残留变形的测量。 以1^-3 kN/s的速度加载，加载至2/3试验荷载，然后卸载 此过程重复进行5次。 第一次加载前与第5次加载后的变形之差为残留变形，其值不允许超过表4中的规定。 6. 3.4.3 以上述相同的速度加载至表4规定的试验荷载，5 min后卸载，井盖、支座不应出现裂纹。 6.4 耐热性能试验 6.4.1试验装置及要求 高低温试验箱，试验控制温度80℃士20C，试验持续时间168 h(7 d) 试样为井盖 6. 4.2 试验方法 井盖在高低温试验箱中80℃士2℃条件下保持168 h,然后在室温下冷却24 ho测试结果以破坏载 荷的相对变化率表示 6.5 抗冻性能试验 6.5.1 试睑 置及要求 CJ/T 211-2005 高低温试验箱，试验控制温度一40℃士2'C。试样为井盖。 6.5.2 试验方法 样品在高低温试验箱中一40℃士2℃条件下保持48 h，然后迅速取出安放到加载试验装置上，测试 其破坏载荷，结果以相对变化率表示。 6.6 耐候性能试验 6.6. 1 试验装置及要求 氮灯气候模拟试验箱，要求有调温调湿装置、喷水装置、氮弧灯光源装置。 6.6.2 试验方法 井盖在氛灯照射及雨淋的条件下持续500 h后，在常温下室内放置24 h,测试结果以破坏载荷的相 对变化率表示。 6.6.3 试验条件: a) 氮弧灯照射温度:600C 15 0C ; b) 湿度:65士5%; c) 光照度:550150 W/m'; d) 喷水时间:1810. 5 min，两次喷水之间的无水时间:102士。. 5 min; e) 试样旋转速率:1 r/mina 6.7 抗疲劳性能试验 6.7. 1 试验装置及要求 动态结构试验机，要求具有载荷、位移、应变及计算函数等多种控制模式，设备所能施加的最大载荷 不应低于500 kN, 6.7.2 试验方法 在井盖上施以频率为0. 2 Hz、峰值为70 kN的标准三角波形变动载荷(见图6)，进行2.5X105次 的疲劳循环试验后，在室内放置24 h,测试结果以破坏载荷的相对变化率表示。 变动载荷 (kN) 时间 (s) 7.5 10 图 6 12.5 15 6.7.3 要求 要求疲劳循环试验后，井盖的破坏载荷下降小于5%。在疲劳循环试验的进行过程中，若意外出现 停顿，每次停顿时间不得超过5 min且一个井盖试验时不应有超过3次的停顿，否则必须更换井盖重新 开始。 检验规则 产品检验分为出厂检验和型式检验。 71 批量与抽样 按批量采用随机抽样方法取样。 产品以同一规格、相同原材料在相同条件下生产的检查井盖构成批量。生产批量:以300套为一 6 CJ/T 211-2005 批，不足该数量时按一批计。 7.2 出厂检验项目 包括产品尺寸偏差、外观质量和强度检验。 7.2.1按5.3^ -5. 9的要求，对检查井盖、井圈逐一检查。 7.2.2 承载能力试验时，每批产品随机抽取3套进行承载能力试验。如有一套不符合5. 10的要求，则 再抽取3套，重复本项试验。如再有一套不符合要求，则该批检查井盖为不合格。 7.2.3 每批产品必须有该批材质的检验 报告 软件系统测试报告下载sgs报告如何下载关于路面塌陷情况报告535n,sgs报告怎么下载竣工报告下载 。 7.3 型式检验 7.3. 1 有下列情况之一时，应进行型式检验: a) 新产品投产前鉴定; b) 正常生产情况下每两年至少进行一次; c) 原料、设备及生产工艺发生变化时; d) 产品长期停产后，恢复生产时; e) 出厂检验结果与上次型式检验有较大差异时; f) 国家质量监督检验机构提出进行型式检验时。 7.3.2 按6. 2的要求检测材料性能，材料性能有一项不合格，则该批产品不合格。 7.3.3按5. 3--5. 9的要求，对某一批量随机抽取5%逐套检查。如果有3套及以下不符合要求，则该 批产品可视为合格。有3套以上不符合要求，则该批井盖不合格。 7.3.4 从7.3.3抽取的检查井盖中，随机抽取3套进行承载能力试验。如有一套不符合5. 10的要求， 则再抽取3套重复本项试验。如再有一套不符合要求，则该批检查井盖不合格。 7.3.5 从7.3.3抽取的粉查井盖中，随机抽取3套进行耐热试验。如有一套破坏载荷下降>5%，则再 抽取3套重复本项试验。如再有一套不符合要求，则该批检查井盖不合格。 7.3.6 从7.3. 3抽取的检查井盖中，随机抽取3套进行抗冻试验。如有一套破坏载荷下降>5%，则再 抽取3套重复本项试验。如再有一套不符合要求，则该批检查井盖不合格。 7.3.7 从7.3. 3抽取的粉查井盖中，随机抽取3套进行耐候试验。如有一套破坏载荷下降>5%，则再 抽取3套重复本项试验。如再有一套不符合要求，则该批检查井盖不合格。 7.3.8从7.3. 3抽取的检查井盖中，随机抽取3套进行抗疲劳试验。如有一套破坏载荷下降>5%，则 再抽取3套重复本项试验。如再有一套不符合要求，则该批检查井盖不合格。 7.4 型式检验不合格时，该产品应立即停止生产。采取措施后，须再次进行型式检验，合格后方能正式 投 入生产。 标志、合格证和贮存、运输 8.1 标志 8.1.1 每个井盖上必须具有清楚且永久性的下列标志: a) 检查井盖专用编号; b) 制造厂名或商标; c) 生产年、月。 8. 1.2 每个支座上必须有清楚且永久性的下列标志: a) 检查井盖专用编号; b) 生产年、月。 8. 1.3 每个合格的井盖、支座上必须有检验人员打的合格标记 8.2 合格证 出厂产品应配有合格证，合格证应包含以下内容: CJ/T 211- 2005 a) 生产厂家; b) 该批产品的名称、规格、数量; c) 注明符合的检验标准(本标准); d) 合格证编号; e) 检验员章; f)检验部门章或检验专用章; 8) 出厂日期。 8.3 贮存 a) 在仓库或露天按规格分类堆放; b)贮存地应远离火源和热源，环境温度不应高于600C, 日.4 运输和装卸 运输时无需包装。人工装卸时，严禁扔上扔下，以免损坏;当用叉车装卸时，层高不应高于十层，产 品底部应有托架。