常用材料泊松比

常用材料泊松比摩擦系数━━━━━━━━━━━━━━━━━━━━━━━━摩擦副材料无润滑摩擦系数μ有润滑────────────────────────钢-钢0.15*0.1-0.12*0.10.05-0.1钢-软钢0.20.1-0.2钢-不淬火的T80.150.03钢-铸铁0.2-0.3*0.05-0.150.16-0.18钢-黄铜0.190.03钢-青铜0.15-0.180.1-0.15*0.07钢-铝0.170.02钢-轴承合金0.20.04钢-夹布胶木0.22-钢-钢纸0.22-钢-冰0.027*-0.014石棉基材料-铸铁或钢0.25-0.400.08-0.12皮革-铸铁或钢0.30-0.500.12-0.15材料(硬木)-铸铁或钢0.20-0.350.12-0.16软木-铸铁或钢0.30-0.500.15-0.25钢纸-铸铁或钢0.30-0.500.12-0.17毛毡-铸铁或钢0.220.18软钢-铸铁0.2*,0.180.05-0.15软钢-青铜0.2*,0.180.07-0.15铸铁-铸铁0.150.15-0.160.07-0.12铸铁-青铜0.28*0.16*0.15-0.210.07-0.15铸铁-皮革0.55*,0.280.15*,0.12铸铁-橡皮0.80.5皮革-木料0.4-0.5*-0.03-0.05铜-T8钢0.150.03铜-铜0.20-黄铜-不淬火的T8钢0.190.03黄铜-淬火的T8钢0.140.02黄铜-黄铜0.170.02黄铜-钢0.300.02黄铜-硬橡胶0.25-黄铜-石板0.25-黄铜-绝缘物0.27-青铜-不淬火的T8钢0.16-青铜-黄铜0.16-青铜-青铜0.15-0.200.04-0.10青铜-钢0.16-青铜-夹布胶木0.23-青铜-钢纸0.24-青铜-树脂0.21-青铜-硬橡胶0.36-青铜-石板0.33-青铜-绝缘物0.26-铝-不淬火的T8钢0.180.03铝-淬火的T8钢0.170.02铝-黄铜0.270.02铝-青铜0.22-铝-钢0.300.02铝-夹布胶木0.26-硅铝合金-夹布胶木0.34-硅铝合金-钢纸0.32-硅铝合金-树脂0.28-硅铝合金-硬橡胶0.25-硅铝合金-石板0.26-硅铝合金-绝缘物0.26-钢-粉末冶金0.35-0.55*-木材-木材0.4-0.6*0.1*0.2-0.50.07-0.10麻绳-木材0.5-0.8*-0.545号淬火钢-聚甲醛0.460.01645号淬火钢-聚碳酸脂0.300.0345号淬火钢-尼龙9(加0.570.023%MoS2填充料)45号淬火钢-尼龙9(加0.480.02330%玻璃纤维填充物)45号淬火钢-尼龙10100.039-(加30%玻璃纤维填充物)45号淬火钢-尼龙10100.07-(加40%玻璃纤维填充物)45号淬火钢-氯化聚醚0.350.03445号淬火钢-苯乙烯0.35-0.460.018-丁二烯-丙烯腈共聚体(ABS)━━━━━━━━━━━━━━━━━━━━━━━━注:1.表中滑动摩擦系数是试验数值,只能作为近似计算参考.2.表中带"*"者为静摩擦系数.各种工程用塑料的摩擦系数━━━━━━━━━━━━━━━━━━━━━━━━━━下试样上试样(钢)上试样(塑料)静摩擦动摩擦静摩擦动摩擦(塑料)系数μs系数μk系数μs系数μk──────────────────────────聚四氟乙烯0.100.050.040.04聚全氟乙丙烯0.250.18--低密度聚乙烯0.270.260.330.33高密度聚乙烯0.180.08-0.120.120.11聚甲醛0.140.13--聚偏二氟乙烯0.330.25--聚碳酸酯0.600.53--聚苯二甲酸乙0.290.280.27*0.20*二醇酯聚酰胺(尼龙66)0.370.340.42*0.35*聚三氟氯乙烯0.45*0.33*0.43*0.32*聚氯乙烯0.45*0.40*0.50*0.40*聚偏二氯乙烯0.68*0.45*0.90*0.52*━━━━━━━━━━━━━━━━━━━━━━━━━━注:*表示粘滑运动.常用材料的滚动摩擦系数━━━━━━━━━━━━━━━━━━━━摩擦副材料滚动摩擦系数k,cm────────────────────淬火钢-淬火钢0.001铸铁-铸铁0.05木材-钢0.03-0.04木材-木材0.05-0.08铁或钢质车轮-木面0.15-0.25钢质车轮-钢轨0.05━━━━━━━━━━━━━━━━━━━━注:表中滚动摩擦系数是试验值,只能作近似参考.材料弹性模量及泊松比━━━━━━━━━━━━━━━━━━━━━━━━━名称弹性模量E切变模量G泊松比μGPaGPa─────────────────────────镍铬钢20679.380.25-0.30合金钢20679.380.25-0.30碳钢196-206790.24-0.28铸钢172-2020.3球墨铸铁140-15473-760.23-0.27灰铸铁113-157440.23-0.27白口铸铁113-157440.23-0.27冷拔纯铜12748轧制磷青铜113410.32-0.35轧制纯铜108390.31-0.34轧制锰青铜108390.35铸铝青铜10341冷拔黄铜89-9734-360.32-0.42轧制锌82310.27硬铝合金7026轧制铝6825-260.32-0.36铅1770.42玻璃55220.25混凝土14-234.9-15.70.1-0.18纵纹木材9.8-120.5横纹木材0.5-0.980.44-0.64橡胶0.007840.47电木1.96-2.940.69-2.060.35-0.38尼龙28.310.10.4可锻铸铁152拔制铝线69大理石55花岗石48石灰石41尼龙101010.7夹布酚醛塑料4-8.8石棉酚醛塑料1.3高压聚乙烯0.15-0.25低压聚乙烯0.49-0.78聚丙烯1.32-1.42徐有邻等[为研究钢筋与混凝土之间的胶结摩阻性能，采用轧制钢板进行了不同锈蚀状况的钢材与混凝土的胶结剪切试验和摩阻试验，试验结果见下表，试验结果表明，胶结剪切强度和摩阻系数随着钢管表面状况的不同变化很大，经过打磨除锈后表面无锈蚀光滑的钢管的胶结强度和摩阻系数明显比有锈蚀的钢管的胶结强度和摩阻系数要低。表面锈蚀程度无锈轻锈重锈腐锈锈蚀特征手感光滑，少量锈蚀，可用干布擦净手感粗糙，砂纸打磨后基本平整颗粒状锈蚀，砂纸打磨后局部有锈坑片状锈渣，砂纸打磨后表面布满锈坑粗糙度0.025～0.0400.050～0.1700.170～0.3400.230～0.660胶结剪切强度0.4350.5680.7580.762摩擦系数0.20～0.250.26～0.300.40～0.500.45～0.60从上式看出，最小值为0.2，但文中未交代粗糙度的单位，如按常规粗糙度单位μm理解，普通钢板的粗糙度Ra为6.3~12.5，也就是说摩擦系数可以取到0.6。根据另一篇参考文献的实验结果，钢板与水泥块的摩擦系数为0.76，有水时为0.7经过多篇文献的互相验证，普通钢板与混凝土的摩擦系数应该可以取0.6计算时考虑安全系数，可适当降低。